玻璃纤维耐碱网布
FIBRE GLASS ALKALI-RESISTANT MESH FABRIC

P30

　　玻璃纤维耐碱网布是以中碱、无碱玻璃纤维机织物为基础，经丙烯酸共私自胶液处理而成。该产品强度高，耐碱性能优良，与树脂粘结性好，服贴性、定位性极佳。主要应用于水泥、塑料、石膏、石材、墙体材料、屋面材料的增强，是建筑行业理想的工程材料。

　　The fiberglass alkali-resistant mesh fabrec,based on C-glassor E-glass woven fabric and coatcd by acrylic acid eopolymerliquid,possesses the properties of rine alkali-resistant,high strength,good cohesion with resin,excellent in locating,etc.Aan ideal engineering material in con-Struction,it is mainly used toreinforce cement,plastic,pitch,stone,wall materials,roofimg and so on.

耐碱涂覆处理玻璃纤维网格布规格基础
Fibre glass alkali-resistant mesh fabric specification base

	纱线密度Tex			经纬密度 (FABRIC COUNT) 根/MM		处理织物厚度 THICKNESS AFTER COATING M+8%	织物质量 FABRIC MASS G/m	处理织物质量 MASS AFTER COAATING G/m	抗拉强力 TENSILE STRENGTH N/5CMX20CM		织物组织结构 FABRIC (PLAIN)	含胶量 LATEX %
	纱线密度Tex			经纬密度 (FABRIC COUNT) 根/MM					抗拉强力 TENSILE STRENGTH N/5CMX20CM
	经线 WARP	纬线 WEFT	经线 WARP		纬线 WEFT				经线 WARP	纬线 WEFT
CAG57-6×5	88	132		6	5	0.27	47	57	500	650	纱罗(LENO)	18
CAP60-20×10	172	68		20	10	0.15	54	60	650	650	纱罗(LENO)	10
CAG65-5×5	132	132		5	5	0.27	53	65	660	660	纱罗(LENO)	18
CAG70-6×5	132	132		6	5	0.29	58	70	750	700	纱罗(LENO)	18
CAG70-8×8	50	132		8	8	0.25	58	70	400	1050	纱罗(LENO)	18
CAG80-6×5	132	165		6	5	0.29	65	80	750	850	纱罗(LENO)	18
CAG85-8×8	88	132		8	8	0.28	70	85	700	1050	纱罗(LENO)	18
CAG90-8×6	132	132		8	6	0.29	74	90	1050	800	纱罗(LENO)	18
CAG90-6×6	132	165		6	6	0.30	72	89	750	900	纱罗(LENO)	18
CAG128-5×5	264	264		5	5	0.62	105	128	1300	1300	纱罗(LENO)	18
CAG128-2.5×2.5	528	528		2.5	2.5	0.52	105	128	1300	1300	纱罗(LENO)	18
CAG143-5×5	264	300		5	5	0.36	118	143	1300	1650	纱罗(LENO)	18
CAG143-2.5×2.5	594	594		2.5	2.5	0.59	118	143	1480	1480	纱罗(LENO)	18
CAG173-5×4	396	396		5	4	0.55	142	173	1980	1580	纱罗(LENO)	18